The molds introduced here are for candle making and are of caprolon engineering.They can be used for casting wax, paraffin, and other bases.The material is resistant to high and low temperatures, so the forms do not crack or split during usage.Caprolon can contact with paraffin additives and acidic environments without any harm.Due to the caprolon's durability, the candle molds can be used unlimited number of times. We have a wide variety of molds for candle making. With their help, you can easily create both traditional and original products with unique designs.

1.The surface can be porous due to low pouring temperature (below140°F degrees),or because of the poor wax quality.Make sure to follow the recommended wax temperature before pouring.

2.The gloss on the surface may not be formed because the pouring temperature is lower than the recommended one. The higher the casting temperature, the glossier the surface of the finished candle is.Do not exceed the pouring temperatures recommended for the candle base used, as this may cause leakage of the candle mass and difficulty when pulling the candle out of the mold. Make sure you also do not exceed the maximum temperature allowed for molds (176 °F), since they may be deformed

3.It is normal if a well is formed after the product is finished. Candle mass expands when heated and decreases during solidification, so after its melting and gradual cooling, there is a well that is formed in the center of the candle.

4.The candle is sometimes removed from the mold with difficulty. It happens if the wax is heated to high temperatures, and there is an increase in the grip. The higher the temperature, the more cohesion is created and therefore it is more difficult to get the finished candle out of the mold. To avoid difficulties in removing, the mold needs to be lubricated before pouring and the temperature should not exceed the maximum allowed for the candle base you are using.